Enhancing strength and creep resistance of Mg-Gd-Y-Zn-Zr alloy by substituting Mn for Zr
Enhancing strength and creep resistance of Mg-Gd-Y-Zn-Zr alloy by substituting Mn for Zr
基本信息来源于合作网站，原文需代理用户跳转至来源网站获取
摘要：
The age-hardening behavior and mechanical properties of the extruded Mg-2Gd-1.2Y-0.5Zn(at.%)alloy with Zr or Mn additions were investigated.The results show that Mn added alloy exhibits more remarkable age-hardening response than Zr added alloy,which is attributed to the fact that partitioning of Mn into the β'phases,β'precipitates and long period stacking ordered(LPSO)phases leads to the decrement in(G d+Y)concentrations in the second phases,facilitating the precipitation during aging treatment.Both peak-aged alloys show bimodal microstructure comprising the fine DRXed grains with nano-sized β phases pinned at DRXed grain boundaries as well as coarse worked grains with strong fiber texture.High strength and good thermal stability were obtained in both peak-aged Mn and Zr added alloys.While the peak-aged Mn added alloy shows higher strength and superior creep resistance due to its denser β'precipitates,thin LPSO phases and γ'precipitates and higher area fraction of worked grains with strong fiber texture.The 0.2% tensile proof stress and ultimate tensile strength of peak-aged Mn added alloy reach up to 454 MPa and 508 MPa,respectively,with elongation of 3.2%at room temperature.The minimum creep rate of the peak-aged Mn added alloy at 250℃/150 MPa is 2.4 × 10^-8 s^-1,which is superior than previously reported extruded Mg-Gd based alloys.
推荐文章
Mg-Gd-Y-Zn-Zr合金冲击断裂机理研究
稀土镁合金
冲击性能
冲击韧性
断裂机理
断口形貌
AC8A铝合金
基于改进Johnson-Cook模型的Mg-Gd-Y-Zn-Zr合金高温流变行为研究
Mg-Gd-Y-Zn-Zr合金
流变行为
Johnson-Cook模型
低Gd含量Mg-Gd-Y-Zr-Zn镁合金组织及性能
Mg-Gd-Y镁合金
时效
组织
力学性能
降温往复镦粗-挤压对Mg-Gd-Y-Zn-Zr合金微观组织的影响
大塑性变形
往复镦粗-挤压
降温变形
Mg-Gd-Y-Zn-Zr合金
内容分析
关键词云
关键词热度
相关文献总数
(/次)
(/年)
引文网络
引文网络
二级参考文献 (0)
共引文献 (0)
参考文献 (0)
节点文献
引证文献 (0)
同被引文献 (0)
二级引证文献 (0)
2019(0)
- 参考文献(0)
- 二级参考文献(0)
- 引证文献(0)
- 二级引证文献(0)
研究主题发展历程
节点文献
Magnesium
alloys
Rare
earth(RE)
PRECIPITATION
Mechanical
properties
Creep
resistance
研究起点
研究来源
研究分支
研究去脉
引文网络交叉学科
相关学者/机构
期刊影响力
镁合金学报（英文）
主办单位：
China
Association
for
Science
and
Technology
Chinese
Committee
for
Magnesium
and
its
Applications
出版周期：
季刊
ISSN：
2213-9567
CN：
50-1220/TF
开本：
出版地：
174 Shazheng Str., C
邮发代号：
创刊时间：
语种：
出版文献量（篇）
153
总下载数（次）
1
总被引数（次）
0
期刊文献
相关文献
推荐文献
- 期刊分类
- 期刊（年）
- 期刊（期）
- 期刊推荐